6010 Aluminium alloy has Aluminium as the major element, and has silicon, magnesium, manganese and zinc as minor elements. [1]
Chemical composition
Element [1]
|
Weight Percentage (%)
|
Aluminum
|
97.3
|
Silicon
|
1
|
Magnesium
|
0.80
|
Manganese
|
0.5
|
Copper
|
0.35
|
Mechanical Properties
Properties [1]
|
Metric
|
Tensile strength
|
290 MPa
|
Yield strength
|
170 MPa
|
Elastic modulus
|
69 GPa
|
Poisson's ratio
|
0.33
|
Elongation at break
|
24%
|
Thermal Properties
Thermal Properties [2]
|
Metric
|
CTE, linear
|
21.5 μm/m-°C
@Temperature -50.0 - 20.0 °C
|
Specific Heat Capacity
|
0.890 J/g-°C
|
Thermal Conductivity
|
151 W/m-K
|
Melting Point
|
585 - 649 °C
|
Solidus
|
585 °C
|
Liquidus
|
649 °C
|
References
- ^ a b c "6010 Aluminium alloy". 25 April 2013. Archived from the original on 2020-08-07.
- ^ "6010 thermal properties". Archived from the original on 2021-01-21.
|
---|
Introduction | |
---|
Al 1000 series (Pure) | |
---|
Al-Cu 2000 series | |
---|
Al-Mn 3000 series | |
---|
Al-Si 4000 series |
- 4006
- 4007
- 4015
- 4032
- 4043
- 4047
- 4543
|
---|
Al-Mg 5000 series | |
---|
Al-Mg-Si 6000 series | |
---|
Al-Zn 7000 series | |
---|
8000 series (Misc.) |
- 8006
- 8009
- 8011
- 8014
- 8019
- 8025
- 8030
- 8090
- 8091
- 8093
- 8176
|
---|
Named alloys | |
---|